By R.J. Pierce & John Bozzelli
I. Introduction
Some operating conditions may generate levels of static electricity on thermoplastic pellets that can cause significant operating problems. These problems may manifest themselves as separation of lines, irregular product feeding or separation of blends of different materials, such as color concentrates in natural resins. These problems can be present in extrusion, injection molding or blow molding operations, in other words, in any processing operation where granulated resins are handled enough to generate static charges.
There is a need for a surface additive that can be added centrally to reduce the effects of this buildup of static electricity to the point of eliminating these problems.
This paper presents work that demonstrates that polyethyleneglycol of the proper molecular weight can be used on polystyrene, SAN, and ABS products to reduce static without damaging the physical practices of the end product.
II. Discussion
Polyethyleneglycol 400 molecular weight (hereafter 400MW) was selected as a possible anti-static agent because it had demonstrated an ability to reduce static buildup when used for industrial applications. It also had demonstrated an ability to be mixed easily onto the surface of the pellets and not to cause splay during molding.
Samples of ABS resins were shipped to a testing laboratory where a continuous airway loop was available. Color blending equipment was used to make up blends of ABS high gloss and transparent ABS resins with several color concentrates. The samples were then dried in desiccated resin dryers for three hours at 180°F. The samples were then put into the airway loop, one sample at a time, and conveyed continuously for extended periods of time (see Fig.1 – Airway Test Loop).
At the end of the airway loop, the material dropped from a vacuum receiver through a clear plastic surge hopper and then into a fiber pack, where a vacuum wand would again pick up the material and send it back around the airway loop again. It was apparent, after a few minutes of operation, that there was a buildup of static electricity on the product as some resin, and a large quantity of color concentrate, would begin to buildup on the clear plastic surge hopper.
At this point a measured amount of polyethyleneglycol 400 MW would be slowly added to the system. The amount was base on 100 parts per million (ppm) of the total resin and color concentrate in the system. There was, in each case, an immediate elimination of the material clinging to the sides of the clear plastic surge hopper. The system would continue to run for several minutes. There was no recurrence of the buildup.
Samples were prepared of resin and color concentrate with and without 100ppm of polyethyleneglycol 400MW, for physical property testing. The actual results of these tests can be seen in Appendix A – Physical Properties Test Results. There was no significant effect on physical properties.
Other molecular weight polyethyleneglycol products were tried for this purpose. Even though lower molecular weight products will control static electricity, they have lower boiling points and can cause splay when used in SAN and ABS resins.
III. Conclusions
A. Polyethyleneglycol 400MW can be used as a surface additive to control the buildup of static electricity in blends of thermoplastic resins at a level of 100ppm.
B. Polyethyleneglycol 400MW has also been used as an additive in salt-and-pepper blends of natural resins and color concentrate to reduce the separation of lines from the blend with good success.
C. Polyethyleneglycol with a molecular weight of 400MW is required for use with ABS and SAN to avoid surface splay. High molecular weights are significantly more viscous and are, therefore, more difficult to blend onto granules.
Figure 1 – Airway Test Loop
Appendix A – Physical Properties Test Results
MAGNUM* 9010; 25:1 with 60% TiO2 Color Concentrate
Physical Test |
Without E-400 |
With E-400 |
Izod @ 72°F (inch-lbf) |
4.1 |
4.0 |
Izod @ 0 oF (inch-lbf) |
1.4 |
1.5 |
Tensile Yield (psi) |
5858 |
5937 |
Tensile Rupture (psi) |
4869 |
4785 |
% Elongation |
76.0 |
77.2 |
Modulus x105 (psi) |
3.33 |
3.53 |
Inst. Impact @ 73°F |
470 |
440 |
Inst. Impact @ 0°F |
130 |
120 |
DTUL | ||
Annealed (oF) |
225 |
225 |
Unannealed (oF) |
170 |
173 |
Gardner Impact |
94.7 |
96.2 |
About the Author
John Bozzelli Injection Molding (IM) Solutions 1019 Balfour St. Midland, MI 48640-3227 Phone: 989-832-2424 Fax 989-832-8743 Email: john@scientificmolding.com www.ScientificMolding.com |
John Bozzelli is a graduate of Marietta College (BS) and Ohio University (MS). His studies were interrupted for a stint in Vietnam (US Army, Purple Heart; Silver Star). Twenty years in Dow Plastics provided extensive experience in polymer synthesis, development, production, and processing. John has been a seminar leader with RJG Associates, Injection Molding Magazine, University of Wisconsin Milwaukee, General Polymers and John Klees. Competent in resin characterization and analysis, his specialty is practical, hands-on injection molding training with both small and large machines. National recognition has come through ten patents, over 60 papers covering plastics, processing, machine specifications, and over 12 years on the national seminar circuit. Feature articles such as the “Productivity”; by Plastics World and ”Scientific Molding” by Injection Molding Magazine October, November and December 1997, have highlighted a couple of exemplar case histories. Check out the August 2001 issue for applications of The Universal Set Up Sheet.John is the initiator of Scientific Injection Molding and teaches the plastic’s point of view for design and processing with a passion you will remember. Take some of your valuable time to learn practical molding techniques that improve your profits tomorrow while eliminating the state of ”fire fighting“ currently found in many molding facilities. Let us keep plastic manufacturing strong in North America. |
The views, opinions and technical analyses presented here are those of the author or advertiser, and are not necessarily those of ULProspector.com or UL Solutions. The appearance of this content in the UL Prospector Knowledge Center does not constitute an endorsement by UL Solutions or its affiliates.
All content is subject to copyright and may not be reproduced without prior authorization from UL Solutions or the content author.
The content has been made available for informational and educational purposes only. While the editors of this site may verify the accuracy of its content from time to time, we assume no responsibility for errors made by the author, editorial staff or any other contributor.
UL Solutions does not make any representations or warranties with respect to the accuracy, applicability, fitness or completeness of the content. UL Solutions does not warrant the performance, effectiveness or applicability of sites listed or linked to in any content.